In this paper, using a fully-coupled, three-dimensional electro-thermal device simulator, we study the mechanism of efficiency degradation at high current operation in planar GaN-based light emitting diodes (LED). In particular, the improvement of the efficiency degradation using thicker conductive GaN substrates has been demonstrated. First, it is found that local Joule heating inside thin conduc...
X-ray topographic and chemical etching examination of Si:Ge single crystals containing 1.2 at% and 3.0 at% Ge, together with precise lattice parameter measurements, was performed. Diffraction contrasts in the form of concentric `quasi-circles' (striations), probably due to the non-uniform distribution of Ge atoms, were observed in projection topographs. The etching patterns reveale...
Orthogonal experiments of GaSb films growth on GaAs substrate have been designed and performed by using a low-pressure metal–organic chemical vapor deposition (LP-MOCVD) system. The crystallinities and microstructures of the produced films were comparatively analyzed to achieve the optimum growth parameters. It was demonstrated that the optimized GaSb thin film has a narrow full width at half maxi...
For homogeneous materials, the ultrasonic immersion method, associated with a numerical optimization process mostly based on Newton's algorithm, allows the determination of elastic constants for various synthetic and natural composite materials. Nevertheless, a principal limitation of the existing optimization procedure occurs when the considered material is at the limit of the homogeneous hypothe...
A vertical hot-wall epi-reactor that makes it possible to simultaneously achieve a high growth rate and large-area uniformity has been developed. A maximum growth rate of 250 µm/h is achieved with a mirror-like morphology at 1650 °C. Under a modified epi-reactor setup, a thickness uniformity of 1.1% and a doping uniformity of 6.7% for a 65-mm-radius area are achieved while maintaining a high growt...
The recent advances in epitaxial SiC films' growth on Si are overviewed. The basic classical methods currently used for SiC films' growth are discussed and their advantages and disadvantages are explored. The basic idea and the theoretical background for a new method of the synthesis of epitaxial SiC films on Si are given. It will be shown that the new method is significantly different from the cl...