Superconductor Substrates
Crystal |
Structure |
M.P. |
Density |
Thermal Expansion |
Dielectric constant |
Growth Tech. & max. size |
standard 1or 2 sides epi polished wafer |
oC |
g/ cm3 |
|
|||||
LSAT |
Cubic |
1840 |
6.74 |
10 |
22 |
CZ |
20x20x0.5mm |
(LaAlO3)0.3 -(Sr2AlTaO8)0.7 |
a=3.868 Å |
Ø35mm |
10x10x0.5mm |
||||
LaAlO3 |
Rhombo. |
2100 |
6.51 |
9.2 |
24.5 |
CZ |
Ø3"x0.5mm |
a=3.790 Å |
Ø3" |
Ø2"x0.5mm |
|||||
c=13.11 Å |
|
Ø1"x0.5mm |
|||||
|
|
10x10x0.5mm |
|||||
MgO |
Cubic |
2852 |
3.58 |
12.8 |
9.8 |
Flux |
Ø2"x0.5mm |
a=4.21 Å |
Ø2" |
10x10x0.5mm |
|||||
NdGaO3 |
Orthor. |
1600 |
7.57 |
7.8 |
25 |
CZ |
Ø2"x0.5mm |
a=5.43 Å |
Ø2" |
10x10x0.5mm |
|||||
b=5.50 Å |
|
|
|||||
c=7.71 Å |
|
|
|||||
SrTiO3 |
Cubic |
2080 |
5.12 |
10.4 |
300 |
vernuil |
10x10x0.5mm |
a=3.90 Å |
Ø30mm |
||||||
SrLaAlO4 |
Tetrag. |
1650 |
|
|
16.8 |
CZ |
10x10x0.5mm |
a=3.756 Å |
Ø20mm |
||||||
c=12.63 Å |
|
||||||
YAlO3 |
Orthor. |
1870 |
4.88 |
2 ~ 10 |
16`20 |
CZ |
10x10x0.5mm |
a=5.176 Å b=5.307 Å |
Ø30mm |
||||||
c=7.355 Å |
|
||||||
YSZ |
Cubic |
~2500 |
5.8 |
10.3 |
27 |
Flux |
Ø2"x0.5mm |
a=5.125 Å |
Ø2" |
10x10x0.5m |