Structural and optical characterization of GaSb on Si (001) grown by Molecular Beam Epitaxy

News

Structural and optical characterization of GaSb on Si (001) grown by Molecular Beam Epitaxy

2019-04-17

GaSb epilayers were grown on Si (001) using molecular beam epitaxy via AlSb quantum dots as an interfacial misfit (IMF) array between the Si substrates and GaSb epilayers. The effect of IMF array thickness, growth temperature and post annealing on the surface morphology, structural and optical properties of the GaSb on Si were investigated. Among five different IMF array thicknesses (5, 10, 20, 40 and 80 ML) that were used in this study, the best result was obtained from the sample with a 20 ML AlSb IMF array. Additionally, it was found that although the full width at half maximum (FWHM) and threading dislocation (TD) densities obtained from high resolution x-ray diffraction curves can be improved by increasing the growth temperature, a decrease in the photoluminescence (PL) signal and an increase in the surface roughness (RMS) emerged. On the other hand, the results indicate that by applying post annealing the GaSb epilayer crystal quality can be improved in terms of FWHM, TD density, PL signal or RMS depending on the post annealing temperature. By applying post annealing at 570 °C for 30 min we achieve a FWHM value of 260 arcsec for a 1 μm thick GaSb epilayer on Si (001) and improve the PL signal intensity without worsening the RMS value.

Source:IOPscience

For more information, please visit our website: www.semiconductorwafers.net,

send us email at sales@powerwaywafer.com or powerwaymaterial@gmail.com


Contact Us

If you would like a quotation or more information about our products, please leave us a message, will reply you as soon as possible.