InAs/InSb nanowire heterostructures grown by chemical beam epitaxy

News

InAs/InSb nanowire heterostructures grown by chemical beam epitaxy

2018-07-25

We report the Au-assisted chemical beam epitaxy growth of defect-free zincblende InSb nanowires. The grown InSb segments are the upper sections of InAs/InSb heterostructures on InAs(111)B substrates. We show, through HRTEM analysis, that zincblende InSb can be grown without any crystal defects such as stacking faults or twinning planes. Strain-map analysis demonstrates that the InSb segment is nearly relaxed within a few nanometers from the interface. By post-growth studies we have found that the catalyst particle composition is AuIn2, and it can be varied to a AuIn alloy by cooling down the samples under TDMASb flux.


Source:IOPscience

For more information, please visit our website: www.semiconductorwafers.net,

send us email at angel.ye@powerwaywafer.com or powerwaymaterial@gmail.com




Contact Us

If you would like a quotation or more information about our products, please leave us a message, will reply you as soon as possible.